HASTELLOY® C-22HS® Alloy
A leading distributor for quality Corrosion-resistant & High-temperature Alloys.
Located in Perth, Western Australia. We ship worldwide from stock or indent order.
HASTELLOY® C-22HS® Alloy
A high strength C-type alloy for the Oil and Gas Industries
HASTELLOY® C-22HS® alloy is the premier nickel-chromium-molybdenum, corrosion-resistant material for oil and gas industry use. Cold working of the alloy at levels between 30 and 65% result in high room temperature yield strengths. It exhibits exceptional resistance to sour gas environments and is NACE/ISO approved.
Product Forms
C-22HS® alloy is available in the form of plate, sheet, strip, billet, bar, wire, pipe, and tube. Round products in the form of solid bars are available up to 10" with various amounts of cold work to achieve high strength and toughness by simultaneously retaining the excellent corrosion resistance of the alloy.
Oil & Gas Applications
The data in this document is believed to be useful for applications in the oil & gas industry, or other industries which may require an alloy with excellent corrosion resistance and strength levels higher than “standard” HASTELLOY® C-22HS® alloy. Additional information on C-22HS® alloy may be found in the alloy brochure H-3180.
Available in Three Very High-Strength Conditions
Early testing of C-22HS® alloy was focused on material in the annealed + age-hardened condition where the material was annealed at 1975°F (1079°C) and age-hardened at 1300°F (704°C)/16h/Furnace cool (FC) to 1125°F (607°C)/32h/Air-cool (AC.) In this “standard condition” C-22HS® alloy will typically have strengths around 100 ksi (690 MPa). While this strength level is almost double of “C-type” alloys in the annealed condition, many oil and gas applications require even greater strength. For this reason, a considerable development effort has been generated on C-22HS® alloy in three other “very high strength” conditions:
1) Cold Worked
2) Cold Worked + Age-HardenedA
3) Low Temperature (LT) AnnealedB + Age-HardenedC
A1125°F (607°C)/10h/AC B1850°F (1010°C) C1300°F (704°C)/16h/FC to 1125°F (607°C)/32h/AC
A comparison of yield strengths for the three very high strength conditions is shown below along with that of the annealed and “standard” conditions. Haynes does not recommend use of highly cold worked and aged material because the increase in yield strengths is minimal and the susceptibility to hydrogen embrittlement in severe oil well conditions is increased.
HASTELLOY® C-22HS® alloy is the premier nickel-chromium-molybdenum, corrosion-resistant material for oil and gas industry use. Cold working of the alloy at levels between 30 and 65% result in high room temperature yield strengths. It exhibits exceptional resistance to sour gas environments and is NACE/ISO approved.
Product Forms
C-22HS® alloy is available in the form of plate, sheet, strip, billet, bar, wire, pipe, and tube. Round products in the form of solid bars are available up to 10" with various amounts of cold work to achieve high strength and toughness by simultaneously retaining the excellent corrosion resistance of the alloy.
Oil & Gas Applications
The data in this document is believed to be useful for applications in the oil & gas industry, or other industries which may require an alloy with excellent corrosion resistance and strength levels higher than “standard” HASTELLOY® C-22HS® alloy. Additional information on C-22HS® alloy may be found in the alloy brochure H-3180.
Available in Three Very High-Strength Conditions
Early testing of C-22HS® alloy was focused on material in the annealed + age-hardened condition where the material was annealed at 1975°F (1079°C) and age-hardened at 1300°F (704°C)/16h/Furnace cool (FC) to 1125°F (607°C)/32h/Air-cool (AC.) In this “standard condition” C-22HS® alloy will typically have strengths around 100 ksi (690 MPa). While this strength level is almost double of “C-type” alloys in the annealed condition, many oil and gas applications require even greater strength. For this reason, a considerable development effort has been generated on C-22HS® alloy in three other “very high strength” conditions:
1) Cold Worked
2) Cold Worked + Age-HardenedA
3) Low Temperature (LT) AnnealedB + Age-HardenedC
A1125°F (607°C)/10h/AC B1850°F (1010°C) C1300°F (704°C)/16h/FC to 1125°F (607°C)/32h/AC
A comparison of yield strengths for the three very high strength conditions is shown below along with that of the annealed and “standard” conditions. Haynes does not recommend use of highly cold worked and aged material because the increase in yield strengths is minimal and the susceptibility to hydrogen embrittlement in severe oil well conditions is increased.
Corrosion-resistant and High-temperature alloys from Haynes International.
Specialty Metals supply all manner of Exotic Alloys from Haynes International.
Corrosion-resistant alloys such as HASTELLOY® B-3® alloy HASTELLOY® C-4 alloy HASTELLOY® C-22® alloy, HASTELLOY® C-22HS® alloy, HASTELLOY® C-276 alloy, HASTELLOY® C-2000® alloy, HASTELLOY® G-30® alloy, HASTELLOY® G-35® alloy,
HASTELLOY® HYBRID-BC1® alloy, HASTELLOY® N alloy, ULTIMET® alloy
High-temperature alloys such as HAYNES® 25 alloy, HAYNES® 75 alloy, HAYNES® 188 alloy, HAYNES® 214® alloy, HAYNES® 230® alloy,
HAYNES® 242® alloy, HAYNES® 263 alloy, HAYNES® 282® alloy, HAYNES® 556® alloy, HAYNES® 617 alloy, HAYNES® 625 alloy,
HAYNES® 625SQ®alloy, HAYNES® 718 alloy, HAYNES® HR-120® alloy, HAYNES® HR-160® alloy, HAYNES® HR-224® alloy, HAYNES® HR-235® alloy, MULTIMET® alloy HAYNES® NS-163® alloy, HAYNES® R-41 alloy, HASTELLOY® S alloy, HASTELLOY® W alloy, HAYNES® Waspaloy alloy,
HASTELLOY® X alloy, HAYNES® X-750 alloy
We have full traceability and supply our Material Certs with every order.
Corrosion-resistant alloys such as HASTELLOY® B-3® alloy HASTELLOY® C-4 alloy HASTELLOY® C-22® alloy, HASTELLOY® C-22HS® alloy, HASTELLOY® C-276 alloy, HASTELLOY® C-2000® alloy, HASTELLOY® G-30® alloy, HASTELLOY® G-35® alloy,
HASTELLOY® HYBRID-BC1® alloy, HASTELLOY® N alloy, ULTIMET® alloy
High-temperature alloys such as HAYNES® 25 alloy, HAYNES® 75 alloy, HAYNES® 188 alloy, HAYNES® 214® alloy, HAYNES® 230® alloy,
HAYNES® 242® alloy, HAYNES® 263 alloy, HAYNES® 282® alloy, HAYNES® 556® alloy, HAYNES® 617 alloy, HAYNES® 625 alloy,
HAYNES® 625SQ®alloy, HAYNES® 718 alloy, HAYNES® HR-120® alloy, HAYNES® HR-160® alloy, HAYNES® HR-224® alloy, HAYNES® HR-235® alloy, MULTIMET® alloy HAYNES® NS-163® alloy, HAYNES® R-41 alloy, HASTELLOY® S alloy, HASTELLOY® W alloy, HAYNES® Waspaloy alloy,
HASTELLOY® X alloy, HAYNES® X-750 alloy
We have full traceability and supply our Material Certs with every order.